www.laboshop.com 1 FINO Coil Wire Wire for clasps, spring-hard. For clasps of partial dentures as well as for orthodontic works. Composition in %: Cr 16.0-18.0; Ni 6.5-9.0; Mn 2.0; Si 1.5; Mo 0.8; C 0.08-0.14; P 0.045; S 0.03; rest Fe. ø 0.7 mm, 30 m each 353.102 , ø 0.8 mm, 20 m each 353.112 , ø 0.9 mm, 10 m each 353.122 , ø 1.0 mm, 10 m each 353.132 , 2Scheu-Dental ChromiumRoundWire Wire for clasps, containing nickel, for partial dentures and orthodontic works. Can be lasered and welded. Composition in %: Cr 16.0-19.0; Ni 6.0-9.5; Mn ≤ 2.0; Si ≤ 2.0; Mo ≤ 0.8; C 0.05-0.15; P ≤ 0.045; S ≤ 0.015; rest Fe. Coil hard = 1400-1600 N/mm² each 353.302 ø 0.5 mm, 50 m , 353.312 ø 0.6 mm, 40 m , 353.322 ø 0.7 mm, 30 m , 353.332 ø 0.8 mm, 20 m , 353.342 ø 0.9 mm, 10 m , 353.352 ø 1.0 mm, 10 m , 353.362 ø 1.1 mm, 10 m , 353.372 ø 1.2 mm, 10 m , hard = 1400-1600 N/mm², 500 g each 352.322 ø 0.7 mm , 352.332 ø 0.8 mm , 352.342 ø 0.9 mm , 352.352 ø 1.0 mm , spring-hard = 1800-2000 N/mm² each 353.402 ø 0.5 mm, 50 m , 353.412 ø 0.6 mm, 40 m , 353.422 ø 0.7 mm, 30 m , 353.432 ø 0.8 mm, 20 m , 353.442 ø 0.9 mm, 10 m , 353.452 ø 1.0 mm, 10 m , 353.462 ø 1.1 mm, 10 m , 353.472 ø 1.2 mm, 10 m , spring-hard = 1800-2000 N/mm², 500 g each 352.402 ø 0.5 mm , 352.412 ø 0.6 mm , 352.422 ø 0.7 mm , 352.432 ø 0.8 mm , 352.442 ø 0.9 mm , 352.452 ø 1.0 mm , 352.462 ø 1.1 mm , 352.482 ø 1.2 mm , 3Scheu-Dental MenzaniumRoundWire Wire for clasps, nickel-free, for partial dentures and orthodontic works. Can be lasered and welded. Composition in %: Cr 16.0-20.0; Mn 16.0-20.0; Mo 1.8-2.5; Si ≤ 1.0; N 0.7-1.0; Ni ≤ 0.2; V ≤ 0.2; C ≤ 0.1; P ≤ 0.05; S ≤ 0.05; rest Fe. Coil hard = 1400-1600 N/mm² each 353.508 ø 0.7 mm, 30 m , 353.518 ø 0.8 mm, 20 m , 353.528 ø 0.9 mm, 10 m , 353.538 ø 1.0 mm, 10 m , hard = 1400-1600 N/mm², 500 g each 352.502 ø 0.7 mm , 352.512 ø 0.8 mm , 352.522 ø 0.9 mm , spring-hard = 1800-2000 N/mm² each 353.608 ø 0.5 mm, 50 m , 353.618 ø 0.6 mm, 40 m , 353.628 ø 0.7 mm, 30 m , 353.638 ø 0.8 mm, 20 m , 353.648 ø 0.9 mm, 10 m , 353.658 ø 1.0 mm, 10 m , 353.668 ø 1.2 mm, 10 m , spring-hard = 1800-2000 N/mm², 500 g each 352.612 ø 0.6 mm , 352.622 ø 0.7 mm , 352.632 ø 0.8 mm , 352.642 ø 0.9 mm , 352.652 ø 1.0 mm , 352.662 ø 1.2 mm , 4Forestadent Forestanit Super RoundWire Orthodontic wire made from high-alloy chromium-nickel stainless steel. Composition in %: Cr 16.0-18.0; Ni 6.0-9.0; Mn ≤ 2.0; Si ≤ 1.5; Mo ≤ 0.8; rest Fe. spring-hard = 1850-2050 N/mm² each 707.128 ø 0.7 mm, 30 m , 707.148 ø 0.8 mm, 20 m , 707.168 ø 0.9 mm, 10 m ,
RkJQdWJsaXNoZXIy MTI3MDM=