www.laboshop.com 1 2 3 4 5 1 Hinrichs Japan Super Hard Plaster Type IV. Synthetic, with low setting expansion, edge-stable and resistant. To produce tooth arches, saw, master, die and control models. Physical data: processing time 5-6 min; setting time 10-12 min; setting expansion after 2 h 0.09 %; compressive strength after 1 h 60 N/mm², dry 90 N/mm². bucket, 10 kg each 100.906 super white , 100.916 golden brown , sack, 25 kg each 100.456 super white , 2Hinrichs CAM-Stone N Super Hard Plaster Type IV. For opto-electronic systems. Makes powdering of plaster models redundant. Prevents irritating reflections within the defined wave ranges. Short setting time. For CAD/CAM systems, tooth arches, saw, master, die and control models. Physical data: processing time 4 min; setting time 7-9 min; setting expansion after 2 h 0.06 %; compressive strength after 1 h 60 N/mm², dry 90 N/mm². bucket, 5 kg each 100.816 red brown , 101.032 ivory , bucket, 10 kg each 100.842 red brown , 101.042 ivory , sack, 25 kg each 100.856 red brown , 101.052 ivory , 3Hinrichs Base Plaster Type IV. For base models of die arches, fixation of reline and orthodontic models, for moulds and milling bases. Tension-free models, precise guidance of the pins. Physical data: processing time 3-4 min; setting time 6-8 min; setting expansion after 2 h 0.06 %; compressive strength after 1 h 40 N/mm², dry 65 N/mm². 25 kg each 100.982 natural white , 4Hinrichs Die Keen Super Hard Plaster Type V. Very hard but not brittle. High fitting accuracy. Compensates the contraction of other materials with an increased expansion. For die arches, saw, master, die and control models. Physical data: processing time approx. 6 min; setting time 10-13 min; setting expansion after 2 h 0.18 %; compressive strength after 1 h 40 N/mm², dry 80 N/mm². 22.7 kg each 101.302 green , 5WhipMix Silky-Rock Super Hard Plaster Type IV. Natural plaster. Compatible with all impression materials. Advantages: • Low expansion; • Silky surfaces; • Abrasion-resistant. Physical data: processing time 3-6 min; setting expansion 0.09 %; compressive strength after 1 h 41 N/mm², after 48 h 90 N/mm². 11 kg each 101.609 yellow , 101.629 white , 25 kg each 101.599 yellow , 101.619 white , 101.689 ivory ,
RkJQdWJsaXNoZXIy MTI3MDM=