www.laboshop.com Physical data: density 6.05 g/cm³; flexural strength 1250-1400 N/mm²; CTE 10.0 x 10-6K-1 (25-500 °C); ceramic type 2, class 6. Composition in %: ZrO2 > 93.5; Y2 O3 4.95-5.35; Al2 O3 0.15-0.35; Fe2 O3 0.02-0.25. For open CAD/CAM systems. Pre-coloured. ø 98 mm. with step, height 12 mm each 046.096 A1 , 046.166 A2 , 046.236 A3 , with step, height 14 mm each 046.106 A1 , 046.176 A2 , 046.246 A3 , with step, height 16 mm each 046.112 A1 , 046.182 A2 , 046.252 A3 , with step, height 18 mm each 046.126 A1 , 046.196 A2 , 046.266 A3 , with step, height 20 mm each 046.136 A1 , 046.206 A2 , 046.276 A3 , with step, height 25 mm each 046.149 A1 , 046.219 A2 , 046.289 A3 , without step, height 10 mm each 046.089 A1 , 046.159 A2 , 046.229 A3 , FINOFRAME ZR CAD/CAMBlank Pre-sintered blank made from yttrium oxide stabilised, tetragonal ZrO2 to produce crown and bridge frames in the anterior and posterior area. High hardness and resistance against damages due to a specific grain distribution and the addition of aluminium oxide. Advantages: • Each disc isostatically pressed, thus very homogeneous density; • Free of distortions during sintering; • No formation of cracks; • No chipping during milling; • High strength. Physical data: density 6.05 g/cm³; flexural strength 1400 N/mm²; CTE 10.0 x 10-6K-1 (25-500 °C); ceramic type 2, class 6. Composition in %: ZrO2 > 94; Y2 O3 4.95-5.35; Al2 O3 < 0.15-0.35; Fe2 O3 < 0.1. For open CAD/CAM systems. ø 98 mm. with step, white each 061.816 height 12 mm , 061.736 height 14 mm , 061.746 height 16 mm , 061.756 height 18 mm , 061.766 height 20 mm , 061.779 height 22 mm , 062.139 height 25 mm , without step, white each 061.959 height 10 mm , 061.966 height 14 mm , 061.976 height 18 mm , 061.989 height 22 mm , 062.149 height 25 mm , For Zirkonzahn CAD/CAM system. ø 95 mm. white each 046.299 height 10 mm , 046.306 height 12 mm , 046.316 height 14 mm , 046.326 height 16 mm , 046.336 height 18 mm , 046.346 height 22 mm , 046.359 height 25 mm ,
RkJQdWJsaXNoZXIy MTI3MDM=