2 3 4 1 INVESTING · CASTING · SOLDERING 1 GC Initial Cast NP Porcelain-Bonding Alloy CoCr-based. To produce crowns and bridges. For veneering metal ceramic in the conventional CTE range as well as composite. High corrosion resistance, free of beryllium, indium and gallium. Advantages: • Compatible with all commercially available metal ceramics in the conventional CTE range; • Excellent processing properties e.g. optimum casting behaviour; • Extra fine molecular structure for a smooth and dense surface after the cast; • Reduced oxide formation increases the aesthetic result; • Optimum synergy with other GC products – Fujivest Premium and Fujivest II investment material for optimum casting results and initial MC veneering ceramic for excellent aesthetics. Physical data: elongation limit 475 N/mm²; Vickers hardness 324 HV10; ultimate elongation 3.4 %; modulus of elasticity 194,000 N/mm²; density 8.4 g/cm³; melting interval 1253-1304 °C; casting temperature 1450 °C; CTE 14.1 x 10-6K-1 (25-500 °C), CTE 14.5 x 10-6K-1 (25-600 °C). Composition in %: Co 63; Cr 28; Nb 4; W 3; Si 1; Fe, Mo 1. 1 pack. 013.429 g , 013.436 g , 013.449 g , 2 Ivoclar Vivadent IPS d.Sign 30 Porcelain-Bonding Alloy* CoCr alloy. Advantages: • Reduced hardness; • Easy to cast and process; • Light oxide; • Easy to deflask; • Certified biocompatibility. Physical data: elongation limit 500 N/mm²; Vickers hardness 385 HV10; ultimate elongation 6.0 %; modulus of elasticity 234,000 N/mm²; density 7.8 g/cm³; melting interval 1145-1165 °C; casting temperature 1240-1350 °C; CTE 14.5 x 10-6K-1 (25-500 °C), 14.7 x 10-6K-1 (20-600 °C). Composition in %: Co 60.2; Cr 30.1; Ga 3.9; Nb 3.2; Si, Mo, Fe, B, Al, Li < 1.0. 150 g 1 pack. 009.162 , 3 Ivoclar Vivadent Colado CC Porcelain-Bonding Alloy* CoCr alloy with a wide range of indications. Suitable for single, telescopic and conic crowns, root posts, short and wide span bridges, implant-supported suprastructures and partial dentures. Advantages: • Excellent bond with porcelain and composite; • Very good melting and casting properties for a homogeneous structure; • Pleasant processing and polishing properties; • High corrosion resistance; • Adjusted compatibility to the Ivoclar Vivadent systems. Physical data: elongation limit 500 N/mm²; Vickers hardness 360 HV10; ultimate elongation 9.0 %; modulus of elasticity 198,000 N/mm²; density 8.5 g/cm³; melting interval 1175-1385 °C; casting temperature 1450-1500 °C; CTE 14.2 x 10-6K-1 (25-500 °C). Composition in %: Co 59.0; Cr 25.5; Mo 5.5; W 5.0; Ga 3.2; Si, Nb, Fe, B < 1.0. 1 pack. 008.722 g , 008.738 g , 008.742 g , 4Yeti Solibond C plus Porcelain-Bonding Alloy Nickel- and beryllium-free CoCr alloy with optimised processing characteristics for flow properties as well as casting results. Advantages: • Very thin oxide layer; • Optimum bond to porcelains; • High fitting accuracy; • Can be laser-welded. Physical data: Vickers hardness 280 HV10; ultimate elongation 10.1 %; modulus of elasticity 210,000 N/mm²; density 8.3 g/cm³; melting interval 1310-1370 °C; casting temperature 1430 °C; CTE 13.9 x 10-6K-1 (25-500 °C). Composition in %: Co 63.0; Cr 24.0; W 8.1; Mo 2.9; Si 1.1; Nb 0.9. 1 pack. 009.082 g , 009.092 g , * This item is not available in all countries. Please contact your customer service expert.
RkJQdWJsaXNoZXIy MTI3MDM=