www.laboshop.com 1 2 3 4 5 3Kulzer HeraeniumCE Partial Denture Alloy High-quality CoCrMo alloy for model casting. Nickel-free, high strength and very good elasticity. Excellent flow properties and dimensional stability. Physical data: elongation limit 580 N/mm²; Vickers hardness 380 HV10; ultimate elongation 4 %; density 8.0 g/cm³; melting interval 1330-1380 °C; casting temperature 1530 °C. Composition in %: Co 63.5; Cr 27.8; Mo 6.6; Si 1.0; Mn 0.6; C 0.3; N 0.2. 1 pack. 010.278 g , 4Kulzer HeraeniumEH Partial Denture Alloy For highest requirements to elasticity and spring properties as well as finishing characteristics. Extraordinary repositioning characteristics and increased torsional stiffness. Good laser welding properties. Physical data: elongation limit 620 N/mm²; Vickers hardness 310 HV10; ultimate elongation 7 %; density 8.0 g/cm³; melting interval 1330-1380 °C; casting temperature 1530 °C. Composition in %: Co 63.5; Cr 28.0; Mo 6.5; Si 1.0; Mn 0.6; N 0.25; C 0.15. 1 pack. 010.288 g , 5Kulzer HeraeniumNF Partial Denture Alloy Particularly suitable for delicate constructions. Very good resilience. Physical data: elongation limit 720 N/mm²; Vickers hardness 360 HV10; ultimate elongation 6 %; density 8.0 g/cm³; melting interval 1320-1380 °C; casting temperature 1530 °C. Composition in %: Co 63.35; Cr 29.0; Mo 5.0; Si 1.0; Mn 0.6; Ta 0.5; N 0.3; C 0.25. 1 pack. 010.292 g , 1 Kulzer HeraeniumP Porcelain-Bonding Alloy CoCr alloy for porcelains in the conventional CTE range. For all indications. Easy to polish, very corrosion-resistant and biocompatible. Nickel-, beryllium- and cadmium-free. Good laser welding and soldering properties. Physical data: elongation limit 650 N/mm²; tensile strength 910 N/mm²; Vickers hardness 330 HV10; ultimate elongation 8 %; modulus of elasticity 200,000 N/mm²; density 8.8 g/cm³; melting interval 1305-1400 °C; casting temperature 1550 °C; CTE 13.8 x 10-6K-1 (25-500 °C). Composition in %: Co 59.0; Cr 25.0; W 10.0; Mo 4.0; Si 1.0; Mn 0.8; N 0.2. 1 pack. 010.662 g , 010.672 g , 2Kulzer HeraeniumPw Porcelain-Bonding Alloy Soft CoCr alloy for porcelains in the conventional CTE range. For all indications, very corrosion-resistant. Easy to process due to the low hardness. Nickel-, beryllium- and cadmiumfree. Good laser welding and soldering properties. Physical data: elongation limit 530 N/mm²; Vickers hardness 290 HV10; ultimate elongation 8 %; modulus of elasticity 208,000 N/mm²; density 8.9 g/cm³; melting interval 1320-1400 °C; casting temperature 1550 °C; CTE 14.3 x 10-6K-1 (25-500 °C). Composition in %: Co 55.2; Cr 24.0; W 15.0; Fe 4.0; Si 1.0; Mn 0.8; N < 0.1. 1 pack. 010.682 g , 010.692 g ,
RkJQdWJsaXNoZXIy MTI3MDM=