www.laboshop.com 1 2 * This item is not available in all countries. Please contact your customer service expert. Non-precious metal porcelain-bonding alloys with a large range of indications. Excellent technical and physical properties are the basis for perfect results. This star symbolizes the FINO SUPERIOR line alloys. You will find this symbol on every cast cylinder! 1 FINOBOND SUPERIOR Porcelain-Bonding Alloy* NiCrMo-based, beryllium-free. With extraordinary mechanical properties, can be used in the crown, bridge and double-crown technique. Also suitable for adhesive bridges and suprastructures. Advantages: • Easy to process due to reduced hardness; • Very good porcelain bonding even in case of multiple firing; • High chromium and molybdenum portion, thus very good intraoral stability; • Particularly suitable for flame casting; • Long-term cooling of ceramic is not required; • Optimal laser welding properties. Physical data: elongation limit 340 N/mm²; tensile strength 580 N/mm²; Vickers hardness 195 HV10; ultimate elongation 15 %; modulus of elasticity 170,000 N/mm²; density 8.2 g/cm³; melting interval 1260-1350 °C; coefficient of thermal expansion 14.0 x 10-6K-1 (25-500 °C). Composition in %: Ni 61.0; Cr 26.0; Mo 11.0; Si 1.5. 1 pack. 008.803 g , 008.813 g , 008.823 g , Trial pack 1 pack. 008.81P7 g , 2FINOBOND LF SUPERIOR Porcelain-Bonding Alloy Nickel- and beryllium-free. Specifically developed for veneering with low-fusing porcelains. Applicable in the crown and bridge technique, for combination dentures as well as in the double-crown technique. Advantages: • High mechanic strength; • Good laser welding properties; • Very good casting characteristics for all melting casting procedures; • Extraordinary processing properties. Physical data: elongation limit 660 N/mm²; tensile strength 950 N/mm²; Vickers hardness 315 HV10; ultimate elongation 11 %; modulus of elasticity 200,000 N/mm²; density 8.2 g/cm³; melting interval 1280-1350 °C; coefficient of thermal expansion 15.9 x 10-6K-1 (25-500 °C). Composition in %: Co 33.0; Cr 30.0; Fe 29.0; Mo 5.0; Mn 1.5. 1 pack. 009.003 g , 009.027 g , Trial pack 1 pack. 009.00P7 50 g ,
RkJQdWJsaXNoZXIy MTI3MDM=