www.laboshop.com 1 2 3 4 1 Kulzer Heravest Speed Investment Material Phosphate-bonded, graphite-free, for crowns and bridges in precious metal and non-precious metal alloys. Speed and conventional heating. Physical data: processing time 5-6 min; setting time approx. 9 min; setting expansion 0.65 % with 50 % mixing liquid, 0.9 % with 75 % mixing liquid, 2.1 % with 100 % mixing liquid; thermal expansion 1.0 % with 50 % mixing liquid, 1.1 % with 75 % mixing liquid, 1.2 % with 100 % mixing liquid; compressive strength approx. 6.0 N/mm²; mixing ratio 100 g : 25 ml. powder 1 pack. 402.872 x g , 402.838 x g , 2Kulzer Heravest Onyx Investment Material Phosphate-bonded, graphite-free, for crowns and bridges. Only for non-precious metal alloys. For speed heating and for the program-controlled pre-heating process. Advantages: • Excellent flow properties; • Excellent fitting even with difficult situations; • Very smooth surfaces. Physical data: processing time approx. 7 min; setting time approx. 9.5 min; setting expansion 0.9 % with 50 % mixing liquid, 1.6 % with 75 % mixing liquid, 2.2 % with 100 % mixing liquid; thermal expansion 0.95 %; compressive strength approx. 4.0 N/mm²; mixing ratio 100 g : 22 ml. powder 1 pack. 402.206 x g , 3Kulzer Heravest Premium 2 Investment Material Graphite-free, phosphate-bonded, for crowns and bridges in precious metal alloys. Advantages: • Very smooth surfaces; • Cast with high fitting accuracy; • Without cracks; • Linearly controlled pre-heating also possible. Physical data: processing time 6 min; setting time approx. 8.5 min; setting expansion 0.5 % with 50 % mixing liquid, 0.55 % with 75 % mixing liquid, 0.8 % with 100 % mixing liquid; thermal expansion 0.95 % with 50 % mixing liquid, 1.05 % with 75 % mixing liquid, 1.05 % with 100 % mixing liquid; compressive strength approx. 4,0 N/mm²; mixing ratio 100 g : 22 ml. powder 1 pack. 403.106 x g , 4Kulzer Heravest Saphir Investment Material Phosphate-bonded, graphite-free, for crowns and bridges. Only for precious metal alloys. Speed heating and program-controlled pre-heating process. Advantages: • Excellent flow properties; • Excellent fitting even with difficult situations; • Very smooth surfaces. Physical data: processing time approx. 7 min; setting time approx. 9.5 min; setting expansion 0.6 % with 50 % mixing liquid, 0.9 % with 75 % mixing liquid, 1.8 % with 100 % mixing liquid; thermal expansion linear 1.0 %; compressive strength approx. 3.0 N/mm²; mixing ratio 100 g : 22 ml. powder 1 pack. 402.216 x g ,
RkJQdWJsaXNoZXIy MTI3MDM=