1 2 3 4 5 1 Bego Bellastar XL Investment Material For crowns and bridges. Ideal for precious metal alloys but can also be applied for non-precious metal alloys. Speed and conventional heating. Advantages: • Extremely fine-grained with very good fitting; • Inviscid to creamy consistency with optimum flow properties; • Safe control of expansion with BegoSol K; • Very good deflasking properties, smooth surfaces; • Can be used with or without casting rings, size of moulds freely selectable. Physical data: processing time approx 3.5 min; thermal expansion linear 0.9-1.1 %; total expansion 1.6-2.1 %; compressive strength 5.5-6.0 N/mm²; mixing ratio 100 g : 25 ml. powder 1 pack. 403.932 x g , 403.946 x g , 2Bego BellaSelect Investment Material For crowns and bridges, for speed and conventional heating. For precious and non-precious metal alloys. Advantages: • Speed heating from 700 to 900 °C; • The insertion temperature is specifically adjusted to CoCr alloys; • Pleasant flow properties enable the reproduction of most delicate details; • Precise adjustment and high reproduction of details for crowns to wide-span bridges; • Ideal also for implant-supported structures; • Suitable for all ringless systems regardless of the desired heating method; • Very good deflasking properties. Physical data: processing time approx. 3.5 min; thermal expansion linear approx. 1.1 %; total expansion 2.1 %; compressive strength approx. 5.5 N/mm²; mixing ratio 100 g : 25 ml. powder 1 pack. 404.008 x g , 3Bego Bellavest DR Investment Material Dust-reduced, phosphate-bonded, speed or conventionally heatable precision investment material for crowns and bridges. For precious and non-precious metal alloys. Advantages: • Considerably reduced (min. 50 %) dust formation; • Very short heating process due to a high insertion temperature of up to 900 °C; • Long processing time of approx. 5 minutes; • Precise expansion control and smooth cast surfaces with BegoSol HE. Physical data: processing time approx. 5 min; thermal expansion linear 1.1 %; total expansion linear 1.9-2.5 %; compressive strength 3.8 N/mm²; mixing ratio 100 g : 25 ml. powder 1 pack. 403.682 x g , 403.692 x g , 4Bego Bellavest SH Investment Material Graphite-free precision casting investment material for crowns and bridges, for speed and conventional heating. Universally applicable for precious metal alloys, non-precious metal alloys, pressed all-ceramic and press-on ceramic. Physical data: processing time 4-5 min; thermal expansion linear 0.8-0.9 %; total expansion linear 1.7-2.2 %; compressive strength 4.2-5.1 N/mm²; mixing ratio 100 g : 25 ml. powder 1 pack. 401.582 x g , 401.642 x g , 5Bego Bellavest T Investment Material Phosphate-bonded, graphite-free, for crowns and bridges. For precious metal and non-precious metal alloys. Conventional heating. Advantages: • Excellent fitting accuracy; • Very fine-grained and results in extremely smooth surfaces; • Edge-stable when setting and easy to deflask. Physical data: processing time 3-5 min; thermal expansion linear approx. 1.05-1.3 %; total expansion linear approx. 3 %; compressive strength 7-10 N/mm²; mixing ratio 100 g : 23 ml. powder 1 pack. 403.960 x g , 402.362 x g , INVESTING · CASTING · SOLDERING
RkJQdWJsaXNoZXIy MTI3MDM=